1.
2.
测定了椽竹竹材的理化性质,并与毛竹、青皮竹和绿竹竹材进行了比较分析.结果表明:椽竹各竹龄竹材的基本密度、气干密度和全干密度平均值分别为0.523～0.632 g·cm-3、0.656～0.801 g·cm-3和0.658～0.777 g·cm-3,随着竹龄增长各部位竹材密度表现出增大的趋势,3年生以上椽竹竹材基本密度小于参比竹种毛竹和青皮竹,大于绿竹.3年生以上椽竹竹材的平均气干体积于缩率和全干体积干缩率分别为9.6％和13.6％,大于毛竹;各竹龄椽竹竹材径向干缩率大于弦向干缩率和纵向干缩率.3年生以上椽竹竹材的灰分平均含量小于绿竹和青皮竹,酸不溶木素平均含量与青皮竹接近而小于绿竹,综纤维素含量大于80％,多戊糖、热水抽出物、1％NaOH抽出物平均含量均高于青皮竹和绿竹,而苯-醇抽出物平均含量小于青皮竹和绿竹.综合分析,椽竹作为纸浆材具有较高的利用价值. 相似文献
3.
人工林米老排木材的物理力学性质 总被引：2，自引：0，他引：2
对23年生人工林米老排木材物理力学性质进行了测定和分析.结果表明:木材气干密度、全干密度和基本密度分别为0.577 g/cm3,0.554 g/cm3,0.463 g/cm3,属中等级别.木材全干差异干缩和气干差异干缩分别为1.963和2.442,弦向和径向干缩湿胀差异较大;木材端面、弦面和径面的硬度分别为5 717.0 N,3 963.7 N和3 822.8 N,弦面和径面的抗劈力分别为16和14 N/mm,弦面和径面的顺纹抗剪强度分别为11.6 MPa和11.3 MPa,抗弯强度和抗弯弹性模量分别为132.3 MPa和13 092 MPa,冲击韧性为62.5 kJ/m2,顺纹抗压强度为48.7 MPa;木材综合品质系数为3 909×105Pa,品质系数非常高,属高等级材. 相似文献
4.
对闽楠人工林和天然林木材物理和力学性质进行了测定和比较分析,结果表明:闽楠天然林木材气干密度和全干密度分别为0.721 g.cm-3和0.680 g.cm-3,人工林木材气干密度和全干密度分别为0.572 g.cm-3和0.535 g.cm-3,闽楠天然林木材密度大于人工林且差异达到极显著水平,但人工林木材密度变异系数却小于天然林。闽楠人工林和天然林木材气干状态下体积干缩率分别为4.935%和6.439%,全干状态下分别为9.330%和11.376%,闽楠人工林木材的尺寸稳定性稍差于天然林,但从木材的差异干缩来看,闽楠天然林和人工林相近,分别为1.75和1.76。闽楠天然林木材端面、径面和弦面硬度分别为7 583 N、6 183 N和6 625 N,稍大于人工林,但差异不显著。闽楠天然林与人工林旋切板背面裂隙率分别为53%和67%,单板厚度的偏差人工林和天然林分别为0.08mm和0.09 mm。由此可知,发展闽楠人工林可以得到质量与闽楠天然林相近的板材。 相似文献
5.
利用SilvilScan-3测定瓜多竹气干密度 总被引：1，自引：0，他引：1
利用SilviScan-3测定了瓜多竹竹材的气干密度,并与常规方法的测定值进行了比较分析,以揭示瓜多竹气干密度的变异规律。SilviScan-3和常规方法测定值差异不显著,也具有较强的线性相关性,决定系数(R2)为0.90。SilviScan-3测定的瓜多竹气干密度平均值为0.520 g.cm-3,分布范围为0.239~1.165 g.cm-3;常规方法测定的平均值为0.604 g.cm-3,分布范围为0.450~0.983 g.cm-3。与常规方法相比,SilviScan-3能连续、快速测定,更适合用于研究竹材气干密度的径向变化。按SilviScan-3方法测定结果,瓜多竹气干密度纵向变化规律为:基部小于中部,中部小于稍部;从竹壁内壁到竹壁厚度1/3处,气干密度缓慢增加,自竹壁厚度1/3处至竹壁外壁,气干密度增加幅度较大。 相似文献
6.
7.
8.
《湖南林业科技》2018,(5)
通过对细柄阿丁枫木材的物理及力学性质的测定与分析,结果显示:细柄阿丁枫木材的基本密度为0. 617 g·cm~(-3),气干密度为0. 733 g·cm~(-3),全干密度为0. 737 g·cm~(-3),体积干缩系数为5. 221%,抗弯强度为86. 0 MPa,顺纹抗压强度为54. 6 MPa,顺纹抗拉强度为137. 6 MPa,顺纹抗剪强度为(径向12. 1 MPa和弦向13. 5 MPa),抗劈力(径向46. 7 N·mm~(-1)和弦向56. 4 N·mm~(-1)),冲击韧性189 kJ·m~(-2)。与鹅掌楸、水青冈、伯乐树、黄檀、枫香树、笔罗子6种常见阔叶树种木材力学性质相比,细柄阿丁枫木材的抗弯强度、顺纹抗压强度和顺纹抗剪强度属中等;抗劈力和冲击韧性属上等。 相似文献
9.
10.
11.
Two common wood flooring materials, taun (Pometia spp.) and cumaru (Dipteryx odorata), were used as investigated objects and comparison was made between the two wood species for their density, microstructure, microfibril angle (MFA), cellulose crystallinity and the main chemical composition. Results showed that the density of cumaru was 0.941 g·cm?3, significantly larger than that of taun, 0.737 g·cm?3. The biggest difference of two wood species in microstructures was fiber cells. Fiber cells of cumaru had dense cell walls, almost no cell lumens; while fiber cells of taun had relatively thin cell walls, with apparent cell lumens. The thickness of fiber cell wall of cumaru and taun were 6.80 and 2.82 µm, respectively, and the former is about 2.5 times thicker than the latter. Measured data of MFA indicated that the average MFA of cumaru was 11.7°, smaller than that of taun, 13.4°. The relative crystallinity of cumaru and taun were 54.0 and 50.8%, respectively. The two wood species had the similar holocellulose contents, but the lignin content of cumaru was higher than that of taun, especially that the content of extractive of cumaru was as twice as that of taun. 相似文献
12.
研究调查木薯淀粉和阿拉伯树胶粘合印楝木屑制成压块的特性。压块在千斤顶平均压力为10．7kg·cm^-2制成。木屑与粘合剂的重量比分别为：100：15,100：25,100：35和100：45。测试压块的物理和燃烧特性。压块的物理和燃烧特性的变化随粘合剂的种类和粘结剂的水平而变化佃〈0．05）。结果表明：淀粉为粘合剂压制的木屑压块有较好的性能、密度、耐用性、热值、固碳百分率、低灰和低挥发物分别为0．546g·cm^-3、95．93％、33．09MJ·kg^-1、84．70％、3．35％和11．95％;而阿拉伯树胶为粘合剂压制的木屑压块的密度、耐用性、热值、固碳百分率、低灰和低挥发物分别为0．425g·cm^-3、94.85％、32．76MJ·kg^-1、87．30％、4．45％和8．75％。研制压块是为了得到良好的燃料,当木屑与淀粉和阿拉伯树胶为粘合剂的比例分别为100：25和100：35,能得到最佳木屑压块。 相似文献
13.
Pilodyn在桉树活立木材性质评估中的应用 总被引：1，自引：0，他引：1
测定了建立在广西22个4年生桉树无性系的Pilodyn值、木材基本密度、边材木材密度、心材木材密度和弹性模量。结果表明：Pilodyn值为9．44—15．41mm、木材密度为0．3514-0．4913g·cm^-3、弹性模量在3．94GPa到7．53GPa之间;Pilodyn值在不同处理、不同方向及不同参试无性系间均存在极显著差异。Pilodyn值与各材性指标间的相关系数在-0．433到-0．755之间,呈显著到极显著负相关。研究表明,Pilodyn方法可以预测桉树活立木的木材密度和弹性模量。 相似文献
14.
Fatima Tavares José L. Louzada Helena Pereira 《European Journal of Forest Research》2014,133(1):31-39
The radial variation in wood density in Acacia melanoxylon R. Br. was studied using microdensitometry by sampling 20 trees with a 40-cm diameter class at four sites in Portugal. The measurements were taken from pith to bark at breast height. A. melanoxylon had an average ring density of 0.607 g cm?3, ranging from 0.556 to 0.630 g cm?3. The mean growth was 6.0 mm year?1. Latewood corresponded, on average, to 34 % of the ring width. Between-tree variability at each site was the main source of variation in the density components, representing between 30 and 54 % of the total variation. Between-sites variability represented from 0 to 21 % of the total variation in density components. The environmental effects (site related) were more pronounced on latewood, while the genetic effect (tree related) was more evident in earlywood. Ring width, latewood percentage and heterogeneity index were independent from site, trees in site and age effects. The values of wood density and radial growth revealed that A. melanoxylon can be important as a commercial timber species in Portugal. 相似文献
15.
以超临界CO2萃取得到的常山胡柚外果皮色素粗产品为原料,对其进行初步鉴定,并研究了pH值、温度、光照、金属离子、氧化还原剂等对常山胡柚天然色素稳定性的影响。结果表明;常山胡柚天然色素属于黄酮类物质,用NaNO2-Al(NO3)3比色法进行定量分析得知,色素液中含有黄酮类的量为2.01 g.L-1,该色素在碱性和中性溶液中较稳定,在酸性溶液中不稳定。光照、高温和氧化剂都会对该色素造成破坏;该色素能耐弱还原剂。低浓度Na 的存在会使最大吸光度增加,具有增色作用,高浓度Na 的存在能使最大吸光度降低。随着Zn2 浓度的增加,色素液的色泽明显变淡,吸光度急剧下降。Ca2 、Cu2 影响趋势基本一致,加入的离子浓度小于0.05 mol.L-1时,色素残存率缓慢下降;大于0.05 mol.L-1时,色素残存率有低幅增加趋势。Mg2 的加入会让色素残存率变小。 相似文献
16.
用LI-6400便携式光合作用系统对美国黑樱桃、加拿大黑樱桃、中国山樱桃苗木的净光合速率、气孔导度、胞间CO2浓度等进行了比较测定,结果表明:(1)日平均净光合速率、气孔导度和胞间CO2浓度均是中国山樱桃最大、美国黑樱桃居中、加拿大黑樱桃最小.3种苗木的净光合速率分别为6.381 μmol·m-2·s-1、5.550 μmol·m-2·s-1、4.952 μmol·m-2·s-1,气孔导度分别为0.200 mol·m-2·s-1、0.151 mol·m-2·s-1、0.134 mol·m-2·s-1,胞间CO2浓度分别为251.7 μmol·mol-1、234.7 μmol·mol-1、230.1 μmol·mol-1.(2)3种苗木的净光合速率、气孔导度、胞间CO2浓度均有显著差异.(3)3种苗木净光合速率的日变化相似,都呈单峰曲线,但美国黑樱桃达到峰值的时间在上午10时,早于加拿大黑樱桃和中国山樱桃,后两者达到峰值的时间都在中午12时.胞间CO2浓度的日变化都是从早晨开始逐渐下降,到下午降低到最小值,然后又有所增加,所不同的是,美国黑樱桃苗木下降到最小值的时间较早,在14时,而中国山樱桃和加拿大黑樱桃则较迟,都在16时.气孔导度的日变化趋势相似. 相似文献
17.
树龄对桉树杂交种发热量和其它燃料特性的影响 总被引：2，自引：0，他引：2
For determining the effect of tree-age on the fuel properties of Eucalyptus hybrid, the variability in basic density, calorific value, proximate and ultimate parameters of 2–6 years old trees and mature
trees (20-year-old), grown under short rotation forestry regime, were measured and analyzed. Results show that there was no
significant variation in the basic density of wood for 2–6 year-old Eucalyptus hybrid, with average value of 0.55–0.58 g·cm−3; the calorific value of mature trees was higher than that of lower age trees, but the ash content was much higher in lower
age trees compared to mature trees. No particular trend was observed for volatile matter content and the fixed carbon content
with tree-age. In conclusion, the fuel properties of mature tree were marginally better than trees of lower age. 相似文献
18.
2006年5月至2007年4月在广西凭祥市中国林科院热带林业实验中心伏波实验场,采用塑料网框收集法对米老排、西南桦、红椎、火力楠、马尾松、杉木6种人工林分凋落物的凋落量及凋落节律进行了研究,结果表明:不同树种林分凋落物的动态变化规律不同,凋落量也各异.在6种林分中,叶、杂物的凋落量以米老排最高,分别达4 748.23、1 881.07 kg·hm-2·a-1,西南桦最低,分别为2 641.32、153.88 kg·hm-2·a-1;枝凋落量以马尾松最高,达902.94 kg·hm-2·a-1,杉木最低,仅149.93 kg·hm-2·a-1.林分的年总凋落量也以米老排最高,达7 095.76kg·hm-2·a-1,西南桦最低,仅3 309.05 kg·hm-2·a-1,米老排林分的年总凋落量是西南桦的2.14倍,而红椎、杉木、马尾松、火力楠4种林分的年总凋落量比较相近,为5 555.61～5 864.87 kg·hm-2·a-1,相差不足6%.6种林分年总凋落量的差异极显著,多重比较显示,米老排与另外5个树种比较都达到了极显著差异,红椎和杉木与西南桦、火力楠、马尾松比较达极显著差异;火力楠、马尾松与西南桦比较达极显著差异. 相似文献
19.
试验设计4～11 g·kg-1 8个NaCl浓度梯度,对转PLD/AtNHXI基因抗盐碱三倍体毛白杨进行组培苗抗盐分化试验,设计2～10 g·kg-19个NaCl浓度梯度进行组培苗抗盐生根试验,设计3～12 g·kg-1 10个NaCl浓度梯度对1年生盆栽苗进行抗盐试验,结果表明:在NaCl浓度达8 g·kg-1时,转基因三倍体毛白杨分化培养37 d后,组培苗的叶色、分化芽数及新稍长度开始受到影响,随着NaCl浓度的增大将抑制组培苗分化生长,甚至枯萎死亡;在含NaCl 7 g·kg-1的生根培养基中,培养20 d后,虽然叶色没有受到盐太大的影响,但生根和新稍的生长都开始受到抑制,根系明显的减少;在含NaCl 7 g·kg-1的土壤条件下,盆栽苗培养32 d后,开始表现出盐害症状. 相似文献