共查询到19条相似文献，搜索用时 218 毫秒
1.
《西部林业科学》2017,(4)
通过对新生杨和美杨物理力学性质的测定分析,结果表明,美杨的气干密度为0.399g/cm~3,基本密度为0.347g/cm~3,径向干缩系数为0.183%,弦向干缩系数为0.312%,抗弯弹性模量为7 373.34Mpa,抗弯强度为57.11MPa,顺纹抗压强度为18.36MPa。新生杨的气干密度为0.365g/cm~3,基本密度为0.330g/cm~3,径向干缩系数为0.188%,弦向干缩系数为0.240%,抗弯弹性模量为6 733.68MPa,抗弯强度为51.53MPa,顺纹抗压强度为16.48MPa。综合分析各项指标,美杨的材性优于新生杨的材性。 相似文献
2.
对安庆段长江滩地I-72杨的密度和干缩性进行了研究。结果表明:I-72杨的气干密度、全干密度和基本密度分别为0.454 g/cm3、0.415 g/cm3和0.364 g/cm3;I-72杨木材密度的径向变异为自髓心向外,最初递减,然后再向外层递增;轴向变异为沿树干向上逐渐增加;I-72杨的径向、弦向和体积全干缩率分别为3.917%、8.093%和12.138%,体积干缩系数为0.169,差异干缩为2.107;I-72杨5.3 m高度处的径向、弦向和体积全干缩率测量值均大于1.3 m高度处的测量值。 相似文献
3.
人工林米老排木材的物理力学性质 总被引：2，自引：0，他引：2
对23年生人工林米老排木材物理力学性质进行了测定和分析.结果表明:木材气干密度、全干密度和基本密度分别为0.577 g/cm3,0.554 g/cm3,0.463 g/cm3,属中等级别.木材全干差异干缩和气干差异干缩分别为1.963和2.442,弦向和径向干缩湿胀差异较大;木材端面、弦面和径面的硬度分别为5 717.0 N,3 963.7 N和3 822.8 N,弦面和径面的抗劈力分别为16和14 N/mm,弦面和径面的顺纹抗剪强度分别为11.6 MPa和11.3 MPa,抗弯强度和抗弯弹性模量分别为132.3 MPa和13 092 MPa,冲击韧性为62.5 kJ/m2,顺纹抗压强度为48.7 MPa;木材综合品质系数为3 909×105Pa,品质系数非常高,属高等级材. 相似文献
4.
伞花木木材物理力学性质初步分析 总被引：2，自引：0，他引：2
伞花木木材物理力学性质测定和分析结果表明 :伞花木木材密度中等、变形小 ,其气干密度为 0 5 97g·cm-3 ,基本密度为 0 4 96 g·cm-3 ,体积干缩系数为 0 30 5 ,顺纹抗压强度为 5 1 5 8MPa ,抗弯强度为 118 84MPa ,综合强度为 170 4 2MPa,属于中等 相似文献
5.
6.
以6个杨树无性系木材为研究对象,对杨树的密度及干缩性能进行了分析研究,为杨树木材的加工利用提供依据。结果表明:6个杨树无性系木材基本密度为0.33～0.43 g/cm3,气干密度为0.39～0.51 g/cm3,全干密度为0.37～0.49 g/cm3,密度在不同无性系间差异极显著。50号杨、中林46杨、南杨木材密度沿径向呈逐渐增加的变化趋势,而108杨、N179杨和桑巨杨木材密度呈现先降低后逐渐增加的趋势。杨树无性系木材气干和全干干缩差异均值分别为2.53和2.22,不同无性系间气干干缩率(径向、弦向、体积、干缩差异)和全干干缩率(径向、弦向、体积、干缩差异)差异均极显著。50号杨、N179杨和桑巨杨木材干缩差异沿髓心向外呈现先增加后减小的趋势,中林46杨呈现逐渐增加的趋势,108杨和南杨则是呈现先减小后增加的趋势。相关性分析表明:木材密度与不同状态下干缩差异呈极显著负相关;木材基本密度除与弦向和体积气干干缩率不相关,与其他干缩指标均呈极显著正相关;不同干缩指标之间呈极显著正相关。 相似文献
7.
8.
对闽楠人工林和天然林木材物理和力学性质进行了测定和比较分析,结果表明:闽楠天然林木材气干密度和全干密度分别为0.721 g.cm-3和0.680 g.cm-3,人工林木材气干密度和全干密度分别为0.572 g.cm-3和0.535 g.cm-3,闽楠天然林木材密度大于人工林且差异达到极显著水平,但人工林木材密度变异系数却小于天然林。闽楠人工林和天然林木材气干状态下体积干缩率分别为4.935%和6.439%,全干状态下分别为9.330%和11.376%,闽楠人工林木材的尺寸稳定性稍差于天然林,但从木材的差异干缩来看,闽楠天然林和人工林相近,分别为1.75和1.76。闽楠天然林木材端面、径面和弦面硬度分别为7 583 N、6 183 N和6 625 N,稍大于人工林,但差异不显著。闽楠天然林与人工林旋切板背面裂隙率分别为53%和67%,单板厚度的偏差人工林和天然林分别为0.08mm和0.09 mm。由此可知,发展闽楠人工林可以得到质量与闽楠天然林相近的板材。 相似文献
9.
本文对８２０３号和木材基本性质进行了测定，其结果：基本密度０．３４５ｇ／ｃｍ＾２；气干密度０．４０ｇ／ｃｍ＾２；干缩系数０．３６；纤维长度１３３７μｍ，长宽比５１；综纤维素含量８０％。８２０３号杨适宜制作各种板材及建筑用材，同时也是较理想的制浆、造纸材种。 相似文献
10.
测定了椽竹竹材的理化性质,并与毛竹、青皮竹和绿竹竹材进行了比较分析.结果表明:椽竹各竹龄竹材的基本密度、气干密度和全干密度平均值分别为0.523～0.632 g·cm-3、0.656～0.801 g·cm-3和0.658～0.777 g·cm-3,随着竹龄增长各部位竹材密度表现出增大的趋势,3年生以上椽竹竹材基本密度小于参比竹种毛竹和青皮竹,大于绿竹.3年生以上椽竹竹材的平均气干体积于缩率和全干体积干缩率分别为9.6％和13.6％,大于毛竹;各竹龄椽竹竹材径向干缩率大于弦向干缩率和纵向干缩率.3年生以上椽竹竹材的灰分平均含量小于绿竹和青皮竹,酸不溶木素平均含量与青皮竹接近而小于绿竹,综纤维素含量大于80％,多戊糖、热水抽出物、1％NaOH抽出物平均含量均高于青皮竹和绿竹,而苯-醇抽出物平均含量小于青皮竹和绿竹.综合分析,椽竹作为纸浆材具有较高的利用价值. 相似文献
11.
杨树新无性系木材性质的变异研究 总被引：4，自引：0，他引：4
The wood basic density, cellulose content and fiber form were investigated for all sample trees at breast height (1.3m) in seven poplar clones, and at 0 (butt), 5.6, 9.6, 13.6, 17.6, 19.6 and 21.6 m for clone Nanlin-95 and Nanlin-895, respectively,for providing information on variation patterns of wood density, fiber characteristics and holocellulose content within trees and among clones. The results showed that significant variations about wood density, cellulose content, fiber diameter and the ratio of fiber length to diameter existed among poplar clones examined. Variance analysis indicated that there were significant differences in wood basic density, fiber length, fiber diameter and cellulose content among the growth rings, which had an increasing tendency along the direction from pith to bark. The significant differences also existed in wood basic density, fiber length and fiber diameter at different tree height. The mean wood basic density had a general increase trend with increasing height of trees and the lowest was found at the base, while fiber length and fiber diameter had a general decline pattern with increasing height of trees and the biggest value was observed at the height of 5.6 m. Regression analysis indicated that the relationship between examined wood properties and growth ring number (cambial age), and the relationship between examined wood properties and tree height can be described by polynomial functions. 相似文献
12.
人工林场杨木材性质与生长培育关系的研究 总被引：21，自引：0，他引：21
本文以生长在 3种长江滩地类型 (江滩、洲滩、湖滩 )、3种栽植密度 ( 3m×4m ,4m× 5m ,5m× 6m)下的3个品系速生人工林杨树木材 [欧美杨无性系 72杨 (Populus×euramericacv.I -72 58) ,美洲黑杨无性系 63杨(P .deltiodescv.I-63 51 )和 69杨 (P .deltoidescv.I-69 55) ,以下简称 72杨 ,63杨 ,69杨 ]为对象 ,深入地分析了人工林杨树木材材性与生长培育之间的关系。结果表明 :( 1 )品系对滩地杨树木材材性有较大的影响。安徽新洲洲滩和湖北黄洲江滩上生长的 63杨 ,湖南沅江湖滩上生长的 72杨纤维长度最长 ,微纤丝角最小 ,导管比量最大 ,方差分析表明 :72、63、69杨微纤丝角和主要物理力学性质差异均达显著和极显著。 ( 2 )滩地类型对72、63、69杨木材材性都有或大或小的差异。方差分析表明 :63杨、69杨微纤丝角、基本密度、抗弯强度和干缩率差异显著 ,说明 63杨和 69杨受滩地类型影响较大。 ( 3)栽植密度对 72、63、69杨木材材性的影响因材性指标的不同而不同。对 72、63、69杨来讲 ,栽植密度越大 ,微纤丝角、导管比量增大 ,纤维长度、木纤维比量、木射线比量都减小 ,基本密度、抗弯弹性模量和抗弯强度也越小。方差分析表明 ,72杨和 69杨受栽植密度影响较大 ,63杨受栽植密度影响较小 相似文献
13.
为了解邓恩桉的木材性质,本研究采用排水法和《GB/T 1930-2009》方法测定邓恩桉的生材含水率、年轮宽度以及木材密度。结果表明：全树生材含水率、年轮宽度、生材密度和基本密度均值分别为114.61%、4.73 mm、1.164 g·cm-3、0.522 g·cm-3。随着树高的增加,年轮宽度、木材密度呈-大-小-大‖趋势,生材含水率呈-小-大-小‖趋势;由髓心向外,木材密度逐渐减小,生材含水率逐渐增大,年轮宽度先增加后减小。4个材性指标在树干径向不同位置间差异极显著,在不同树高间差异不显著（除年轮宽度外）。基本密度与3个材性指标间存在极显著或显著相关。 相似文献
14.
15.
川滇桤木的生境适应性、木材纸浆性能与林分生态效益分析 总被引：1，自引：0，他引：1
川滇桤木是一个生态经济型的纸浆原料林树种,适于在亚热带地区重点发展,或与桉树混交及作桉树林退化后的替代种植树种,以实现纸浆原料林的可持续发展。川滇桤木的生境适应性强、生长速度快,除干旱的阳坡不宜种植外,对各种立地环境都较适应,其人工林林木高和径的年均生长量都在1以上。川滇桤木木材的造纸性能良好,其木材密度为0.48 g/cm3,纤维长度1.19 mm,纤维长宽比91.47,综纤维素87.17%,苯醇抽出物2.56%,细浆得率43.6%,黑液残碱7.0 g/mL,撕裂指数8.2 mN.m2/g,抗张指数48.79 N.m/g,耐破指数3.31 kPa.m2/g。川滇桤木具有良好的生态功能,营造人工林后,林分生物多样性增加,林地的水湿条件得到改善,其人工林群落特征与亚热带常绿阔叶林一致,改良林地土壤的效果良好,能提高林地土壤的肥力。 相似文献
16.
17.
18.
黑龙江省主要杨树纤维用材品种纸浆性能综合评价 总被引：1，自引：0，他引：1
选择黑龙江省7个主要杨树纤维用材品种为研究对象,测定了木材纤维形态、化学成分和成浆性能,分析了林龄与主要纸浆性能间的相关关系,对7个品种纸浆性能进行了综合评价。试验结果表明:7个品种的纤维长度为0.88～1.17mm,纤维素含量为49.28%～59.77%,粗浆得率为50.41%～54.97%,上述指标均达到或超过优质纸浆标准;林龄与纤维长度、纤维素含量和粗浆得率间无显著相关关系;纸浆性能综合评价由高至低的顺序为黑青杨>小青黑>银中杨>大青杨>青山杨>小黑杨>迎春5号。 相似文献
19.
采取常规方法对异叶南洋杉木材物理力学性质进行了测定研究,试验结果表明,异叶南洋杉的气干密度、基本密度、绝干密度分别为0.480、0.466、0.4576 g·cm^-3;径向、弦向和体积干缩率平均值分别为2.73%、2.5%和11.25%;干缩系数分别为0.116%、0.095%和0.46%;端面、径面、弦面等三个面的硬度分别为35、18.6和17.7 MPa;顺纹抗压强度平均为36.9 MPa;抗弯弹性模量为9334.36 MPa;冲击韧性为32.63 kg·m^-2;物理力学性质除了体积干缩系数、冲击韧性之外的所有指标都处于第2级,体积干缩系数和冲击韧性分别处于第3级和第1级。 相似文献