 共查询到20条相似文献，搜索用时 406 毫秒
1.
Changes in the modulus of elasticity (MOE), modulus of rupture (MOR), and stress relaxation in the radial direction of wood (hinoki:Chamaecyparis obtusa) moisture-conditioned by the adsorption process from a dry state and by the desorption process from a moisture content slightly below the fiber saturation point were investigated. The MOE and MOR of wood conditioned by the adsorption process showed significant increases during the later stages of conditioning when the moisture content scarcely changed. However, with the desorption process they did not increase as much during later stages of conditioning, though they increased during early stages of conditioning when the moisture content greatly decreased. The stress relaxation of wood decreased with an increase in the conditioning period with both the adsorption and desorption processes. These results suggest that wood in an unstable state, caused by the existing state of moisture differed from that in a true equilibrium state shows lower elasticity and strength and higher fluidity than wood in a true equilibrium state. Furthermore, the present study demonstrates that the unstable states of wood induced during the course of drying, desorption, and possibly adsorption of moisture are slowly modified as wood approaches a true equilibrium state.  相似文献   

2.
Previously we showed that the relaxation modulusEt of water-saturated wood during temperature reduction maintained its initial value despite the decrease in temperature, although during temperature elevationEt showed a marked decrease. In the present study, to clarify the mechanism of relaxation during temperature elevation and reduction, Young's modulus was measured in stress relaxation experiments with changes in temperature, and relaxation behavior was simulated using a Maxwell model consisting of five elements. Furthermore, the dynamic Young's modulus and dynamic loss modulus were measured during both temperature elevation and reduction. The results obtained suggested that the unique relaxation behavior during temperature reduction was caused by decreases in Young's modulus and coefficient of viscosity (i.e., an increase in fluidity) compared with those during elevation of temperature. The decrease in Young's modulus and increase in fluidity were considered to be due to an unstable structure in wood that occurred during temperature reduction. This unstable structure probably develops in the nonequilibrium state of temperature toward a true equilibrium state. Wood should be more unstable during temperature reduction than during temperature elevation because of the decrease in molecular motion when the temperature is lowered.Part of this report was presented at the 49th annual meeting of the Japan Wood Research Society, Tokyo, April 1999  相似文献   

3.
Physical and mechanical properties of wood after moisture conditioning   总被引：1，自引：0，他引：1  
Some properties of wood (hinoki:Chamaecyparis obtusa) moisture-conditioned by an adsorption process from a dry state and by two desorption processes (from a water-saturated state and from a state with a moisture content slightly below the fiber saturation point) were investigated. The moisture contents of wood conditioned by the adsorption process and by the desorption process continued to approach to one another for the moisture-conditioning period of over 50 weeks. Accordingly, sorption hysteresis should be regarded as a transitional phenomenon that occurs during the process of approaching the true equilibrium, which requires a long time. The wood conditioned by the desorption process beginning from a water-saturated state showed slightly smaller dimensions than those conditioned by the adsorption process with the same moisture content; however, the wood conditioned by the desorption process from a moisture content below the fiber saturation point showed slightly larger dimensions than those conditioned by the adsorption process. The wood conditioned by the adsorption process from a dry state showed a higher modulus of elasticity and modulus of rupture than did the wood conditioned from a water-saturated state with the same moisture content. The mechanical properties of the wood also varied based on the states at which the desorption process was started. This is a notable characteristic of the relation between the drying condition and the mechanical properties of wood.  相似文献   

4.
Mechanical property changes due to the moisture content (MC) and/or temperature changes were examined for 15 Indonesian wood species. A static bending test was carried out at 20°C, 65% relative humidity (air-dry), and water-saturated at 20°C (wet-20) and 80°C (wet-80). For individual test conditions, modulus of elasticity (MOE) and modulus of rupture (MOR) increased linearly with specific gravity regardless of wood species; however, maximum deflection did not correlate with specific gravity for any MC or temperature conditions. The relative values of MOE and MOR measured in wet-20 to air-dry conditions were variously affected from slightly to strongly depending on the wood species. However, the relative values always decreased markedly when saturated in water at 80°C, regardless of wood species. The relative MOE, MOR, and maximum deflection values due to the change in MC or MC and temperature combined were independent of specific gravity but may be dependent on wood type: softwood or hardwood.  相似文献   

5.
In order to clarify the effect of drying on structural changes of DMSO swell treated and DEA-SO2-DMSO decrystallization treated Chinese fir （Cunninghamia lanceolate） wood, the stress relaxation of treated oven-dry specimens during the processes of temperature elevation and reduction and that of treated wet specimens at constant temperature were determined. A stress decrease process and a stress increase process were observed in all stress ratio curves of wood during the processes of decreasing temperature. Untreated wood, during the process of temperature reduction under higher initial temperature conditions and during the process of temperature elevation, has a larger stress decrease than treated woods. In a wet state this trend is reversed. It indicated that the drying set made treated woods have a smaller increase in fluidity of wood constituents with increasing temperature. Some bonding between decrystallization reagents and wood molecules may occur.  相似文献   

6.
The dynamic shear modulus and the loss modulus of Betula alba, Ulmus parvifolia, Quercus robur, Acer platanoides, Tilia cordata, Fraxinus excelsior and Pinus sylvestris wood were measured using an inverted torsion pendulum within a wide temperature range. The glass transition temperature of the lignin–carbohydrate complex and the decomposition temperature of the wood cellulose were estimated. The temperature band from 170°C to 240°С shows the transition of the lignin–cellulose complex from the glassy to the rubbery state. Mechanical properties of different types of wood are affected by moisture and anatomical differences, but glass transition and decomposition temperatures are the same. More than 5% of moisture in the wood stored at normal conditions were found. After drying, the increase of dynamic shear modulus of wood over the entire region of the glassy state was observed. The intensity of maximum peak of dynamic loss modulus is also increased due to activation of the segmental motion of macromolecules of the ligno-carbon complex. The decomposition temperature of the cellulose crystallites was unchanged for specimens containing moisture and for dried specimens.  相似文献   

7.
Thermal-softening properties and cooling set of water-saturated bamboo were investigated using stressrelaxation measurements in heating and cooling processes, followed by residual deflection measurement. In the heating process, an obvious decrease in relative relaxation modulus due to thermal-softening of lignin was found at around 60°C. On the other hand, no clear change in the relative relaxation modulus was recognized in the cooling process. After the cooling process, about 65% and 75% of residual set was measured when the specimen was loaded on the epidermis and endodermis side, respectively. Also, residual set depended on the maximum temperature reached in the heating process and the unloaded temperature in the cooling process. From these results, it was deduced that the glass transition of lignin from the rubbery to glassy state is important to fix the deformation. Comparing thermal-softening behavior between bamboo and wood, the relative relaxation modulus of wood decreased steeply at higher temperatures than for bamboo. On the other hand, while about 75% of residual set was also found for wood, almost the same as for bamboo, the recovery of deformation with time was larger for wood than for bamboo. Part of this article was presented at the 53rd Annual Meeting of the Japan Zairyou Society, Okayama, May 2004  相似文献   

8.
The present study examines the three-dimensional hygric and mechanical behavior of oak wood. The moisture equilibrium state, characterized by the sorption isotherms, was obtained from measurements taken during adsorption and desorption cycles. Sorption behavior was analyzed with the Dent theory and compared considering the sorption direction (adsorption/desorption cycle). Sorption parameters were provided for possible numerical applications in hygric material models. The corresponding swelling and shrinkage behavior was examined and characterized by the moisture expansion parameters for all anatomical directions. Orthotropic mechanical material behavior was characterized by determining the elastic engineering (Young's moduli, shear moduli, and Poisson's ratios) and the bending, compressive and compressive shear strength material parameters. Influence of moisture content (MC) on the mechanical material properties was studied using Young's moduli, Poisson's ratios, and the investigated strength parameters. A significant difference between the sorption behavior in adsorption and desorption, known as the hysteresis effect, could be proved. Furthermore, swelling and shrinkage behavior did not show any dependency on the adsorption/desorption cycle. The results confirm the significant influence of MC on the Young's moduli and the strength properties, however, did not validate an influence on the Poisson's ratios.  相似文献   

9.
Stress relaxation of water-saturated wood was examined at various temperatures and during the processes of elevation and lowering of temperature. The difference between relaxation at a lower temperature and that at a higher temperature was almost same as the increase in relaxation during temperature elevation. Similar results were obtained regardless of the elevating speed of the temperature and regardless of preheating the samples. On the other hand, relaxation behavior during temperature lowering was quite different from that during temperature elevation. The relaxation moduli during the process of lowering the temperature scarcely changed, although those at various constant temperatures decreased with increases in temperature. Marked sets occurred after relaxation measurements under temperature lowering, whereas only slight sets occurred during the process of elevating the temperature or at a constant temperature of 80°C. Furthermore, it was found that the sets that occurred during the process of temperature reduction were almost recovered when the samples were heated again in water. The mechanism of the relaxation behaviors observed in the present study under nonequilibrium temperature is discussed in relation to the occurrence of set after relaxation measurements.Part of this report was presented at the 48th annual meeting of the Japan Wood Research Society, Shizuoka, April 1998  相似文献   

10.
In order to investigate the effect of different reagents on changes of the crystalline region and amorphous region (Matrix) in wood cell walls, the creep behavior of Chinese fir (Cunninghamia lanceolata) wood treated with dimethyl sulfoxide(DMSO) and diethyl amine, sulfur dioxide and dimethyl sulfoxide mixture (1)EA-SO2-DMSO), and the untreated wood at oven-dried, air-dry and water-saturated states during adsorption and desorption processes were all examined in air or in water. The measurements were carded out at ambient temperature and atmospheric pressure. The load is constant with 62 g or 0.607 6 N. The results obtained were as follows: 1) The instantaneous compliance J0 and the creep compliance J of specimens decrystallized with DEA-SO2-DMSO solution were bigger than those of DMSO swollen wood, and the latter was still much bigger than those of untreated wood. 2) For untreated wood, J0 and J increased with equilibrium moisture content (EMC) of wood, but there was not apparent correlation between wood EMC and the relative compliance. 3) Specimens treated with DMSO and DEA-SO2-DMSO mixture were recrystallized after immersion in water, and the degree ofrecrystallization of the former was larger. 4) For oven-dried specimens, the creep compliances in water were bigger than those in air. But for fiber-saturated and water-saturated specimens they were nearly equivalent to each other.  相似文献   

11.
This study examined the bending creep behavior of hot-pressed wood during cyclic moisture changes. Sugi (Cryptomerica japonica D. Don) specimens were pressed in the radial direction under six combinations of nominal compressive strain (33% and 50%) and press temperatures (140°C, 170°C, 200°C). Creep tests were conducted at 20°C with three cyclic relative humidity changes between 65% and 95% under 25% of short-breaking stress. The effect of moisture content (MC) change on elastic compliance and mechanosorptive (MS) compliance was investigated. The relation between MS compliance and thickness swelling was studied. The results indicated that total compliance increased over the history of cyclic moisture changes; and its behavior was closely related to the changes in MC and thickness swelling. The total compliance increased during adsorption and decreased during desorption. Elastic compliance increased linearly with MC and was dependent on press temperature and compression. With increasing MC change, MS compliance increased during adsorption and decreased during desorption. The first adsorption led to greater MS compliance than did the subsequent adsorption with the same amount of MC change. In general, the elastic parameterK E and the MS parameterK Mincreased with compression and decreased as the press temperature increased. The MS parameterK M was apparently greater than the elastic parameterK E. The MS parameterK M increased with swelling coefficient KSW of the hot-pressed specimen during adsorption and decreased with an increasing shrinkage coefficientK SH during desorption.  相似文献   

12.
The effects of moisture content from 17 to 159% MC and temperatures from −71°C to +58°C on resonance-based acoustic velocity and dynamic modulus of elasticity (DMOE) were investigated using 36 boards of radiata pine sapwood. Acoustic velocity decreased with increasing moisture content and temperature, although effects differed noticeably below and above fibre saturation point (FSP). Below FSP, acoustic velocity decreased rapidly and linearly with increasing moisture; whereas above FSP changes in velocity were rather gradual and curvilinear with marked differences in velocity patterns between temperatures below and above freezing. Acoustic velocity decreased linearly with increasing temperature but there was an abrupt discontinuity at the freezing point for wood above FSP. Changes in moisture content and temperature affecting wood density and acoustic velocity led to changes in DMOE, although this relationship was not straightforward because changes of velocity with moisture were linear or curvilinear and depended on whether wood was frozen or unfrozen, whereas changes of density with moisture content were invariably linear. For practical work, it is important to estimate the relative effect of changing moisture content or temperature with respect to standard conditions on DMOE, thus general guidelines were devised to account for significant changes.  相似文献   

13.
The influence of moisture content (MC) on the orthotropic viscoelasticity of Chinese fir wood (Cunninghamia lanceolata [Lamb.] Hook.) has been examined in low temperature environment. Storage modulus E′ and loss modulus E″ of wood with six different levels of MC ranging from 0.6 to 22.0% were determined from ??120 to 40 °C and at multi-frequency range of 0.5, 1, 2, 5, and 10 Hz using a TA instruments® Dynamic Mechanical Analyzer (DMA 2980). The results showed that a distinct moisture dependency is exhibited by the orthotropic viscoelastic behaviour of Chinese fir wood. With the exception of some apparent activation energy (ΔE) for β-relaxation process, the E′ decreased and the E″ peak temperatures moved towards lower temperature and the ΔE for α-relaxation process became lower with MC increasing in all orthotropic directions, whereby individual decline of E′ and the E″ peak temperatures were affected by MC to different degrees. Besides, a little E″ peak at around 0 °C was only seen in L direction, which could be attributed to the melting of frozen water. Furthermore, the dynamic viscoelastic behavior of wood is also dependent on the measurement frequency. The findings suggest that the orthotropic structure and moisture content have an important influence on the viscoelastic performance in low temperature environment.  相似文献   

14.
Vibrational properties of heat-treated green wood   总被引：2，自引：0，他引：2  
To investigate the influence of water on heat treatment, green wood was heat-treated. Sitka spruce (Picea sitchensis Carr.) with about 60% moisture content (MC) was used. Young's modulus and loss tangent were measured by the free-free flexural vibration test. The specimens were heated in nitrogen at 160°C for 0.5h. The results were as follows. (1) Recognizing that the effects of heat treatment are mild and that the same specimens cannot be used for both heat treatment and as controls, it was necessary to investigate the effects of the heat treatment based on the variations of properties in the whole of the test lumber. (2) Young's modulus increased and the loss tangent decreased due to heat treatment. When the vibrational properties were measured at various MCs, the MCs at the maximum value of Young's modulus and the minimum value of the loss tangent were lower in heat-treated specimens than in controls. The effects of heat treatment in green wood were similar to those in air-dried wood. (3) The loss tangents of heat-treated specimens were smaller than those of controls at about 0% MC but were larger than those of controls at about 10% MC. We thought that this resulted from the decreased MC at the minimum loss tangent after the heat treatment mentioned above. (4) The properties measured at several MCs were more useful than those at only one moisture content for investigating the effects of heat treatment.This study was presented in part at the 46th annual meeting of the Japan Wood Research Society, Kumamoto, April 3–5, 1996; and at the 47th annual meeting of the Japan Wood Research Society, Kochi, April 3–5, 1997  相似文献   

15.
Moisture sorption tests and compression tangential tests at 25°C were carried out on specimens of mahogany (Swietenia macrophylla King) wood from Peru. The tests were performed over seven adsorption and five desorption moisture conditions, and differences in strength between adsorption and desorption curves at a given equilibrium moisture content were evaluated. The results showed that second-order effects in mahogany wood were not discernible in either the tangential compliance coefficient or for the stress at the proportional limit in tangential compression.  相似文献   

16.
As a follow-up report, the pre-treatment by compression for wood drying was systematically studied in terms of the reduction of moisture content (MC), the recovery rate (RR), and mechanical properties of wood compressed at different MC conditions. The results showed that MC after compression on water-saturated wood determined the critical value of MC before compression which were about 84 and 105% at a compression ratio of 60 and 40% for Poplar and Chinese fir, respectively. Beyond the critical value, MC after compression remained constantly at about 84% and decreased slightly from 105% for Poplar and Chinese fir, respectively. The MC reduction decreased with the decrease of MC before compression. The MC reduction was rather effective when the MC before compression was higher than the critical value and was recommended to pre-treat for the effectiveness of MC reduction. In addition, after the recovery, the wood volume and mechanical properties were well retained for the wood compressed at all MC conditions which were above fiber saturation point (FSP) before and after compression. Therefore, the pre-treatment by compression is viable in terms of the RR and mechanical properties at rather broad MC conditions above FSP. Moreover, the compression force needed for treatment was almost same at these MC conditions.  相似文献   

17.
In order to investigate the effects of chemical components and matrix structure on the destabilization of quenched wood, we examined the physical and mechanical properties of steam-treated wood, hemicellulose-extracted wood, and delignified wood, which were treated at different levels. For steam-treated and hemicellulose-extracted wood,the relative relaxation modulus of the quenched sample was lower than that of the respective control sample. For delignified wood, the relative relaxation modulus fell with weight loss and reached a minimum value at a certain weight loss, and subsequently increased significantly. The hygroscopicity of all treated samples changed slightly by steaming, whereas increased with removing the component. More-over, the average volumetric swelling per 1% MC at 100% relative humidity (RH) was less than at 75% RH and 93% RH for component-removed wood. It was clear that a void structure existed. As a result, the destabilization evaluated by the fluidity (1 - E t/E 0) of steam-treated wood was influenced by the amount of adsorbed water. For component-removed wood, destabilization increased temporarily at lower weight loss because of nonuniform cohesive structure. At high weight loss, destabilization will decreased because capillary-condensed water gathered in the voids and obstructed the motion of adsorbed water. However, the destabilization of all treated wood changed less than that of chemically modified wood.  相似文献   

18.
The modulus of elasticity and the modulus of rupture during static bending in the radial direction, and the viscoelastic properties in the radial direction in the temperature range 20°–100°C of hinoki (Chamaecyparis obtusa) swollen in organic liquids with two or more functional groups in a molecule were compared with those of wood swollen by moisture. The wood swollen in organic liquids in or near the swelling equilibrium, but not that swollen in organic liquids distant from the swelling equilibrium, showed higher moduli of elasticity and rupture than the wood swollen to a similar degree by moisture. This suggests that wood exists in an unstable state as it approaches the swelling equilibrium, rendering it highly flexible and weak. During the first viscoelastic measurements for wood swollen in various organic liquids, thermal softening was observed in 40°–60°C range and above 80°C, though this softening disappeared during the second measurement. The softening observed in the 40°–60°C range and above 80°C was thought to have been caused by the redistribution of liquid toward the equilibrium state at a higher temperature and the swelling accompanying an elevated temperature, respectively.Part of this report was presented at the 49th Annual Meeting of the Japan Wood Research Society, Tokyo, April 1999  相似文献   

19.
In order to understand the reason why glycerin pre-treatment can accelerate the deformation fixation of compressed wood, the interaction between glycerin and wood at various temperatures was investigated in this study from stress relaxation approach. The compression stress relaxation curves of poplar (Populus cathayana Rehd.) samples impregnated with glycerin were measured at temperatures ranging from 25 to 180°C, together with the curves of oven-dry wood at temperatures between 100 and 180°C for comparison. The activation energy was calculated according to the Eyring’s absolute rate reaction theory. The results showed that temperature had very obvious effect on stress relaxation for both glycerin-treated wood (GTW) and oven-dry wood. The stress released very fast at higher temperatures. Glycerin showed an accelerating effect on stress relaxation. At temperatures exceeding 120°C, a complete relaxation of the stress could be expected. While for untreated wood, it cannot be reached until 160°C. By calculating the apparent activation energy (ΔE) of GTW at different temperatures, it is clear that two mechanisms are responsible for different temperature ranges. From 40 to 100°C, ΔE is only 8.24 kJ/mol, which corresponds to the hydrogen bonds formed between wood and glycerin molecules; from 120 to 180°C, ΔE reached 81.38 kJ/mol, which corresponds to the degradation of hemicelluloses or lignin, and during this process, new cross-linking would happen.  相似文献   

20.
The effects of temperature and moisture content on selected mechanical properties associated with the chipping process were evaluated. In chipping, mechanical properties such as shear parallel to the grain, cleavage, and bending are involved. Matched samples of heartwood and sapwood were obtained from freshly harvested logs of black spruce and balsam fir to determine the variation of the studied mechanical properties between ?30 and 20 °C, at intervals of 10 °C. Moisture content (MC), basic density (BD), and annual ring width (RW) were measured for each sample. For both wood species, temperature had a significant effect on all mechanical properties under freezing conditions (below 0 °C). This effect was more important for sapwood than for heartwood, which was explained by the difference in MC between these two types of wood. Between 0 and 20 °C, temperature and type of wood did not show any significant effect on the mechanical properties. Multiple regression models were obtained to predict the mechanical properties. These regressions showed that MC was the most important factor to explain the mechanical properties below 0 °C. However, for temperatures of 0 °C and higher, BD was the principal factor to predict the mechanical properties. RW was not a significant factor to predict any mechanical property. Cleavage was the most sensitive one to changes in temperature followed by shear, modulus of rupture, and modulus of elasticity. These results could be of great importance in the chipping process.  相似文献   