Scratch deformations of poly (ether ether ketone) composites |
|
| Authors: | T Iqbal S Yasin P F Luckham N Ramzan M Mohsin |
| Institution: | 1. Chemical Engineering Department, University of Engineering & Technology, KSK Campus, Lahore, Pakistan 2. Chemical Engineering Department, Imperial College London, SW7 2AZ, London, UK 3. Department of Textile Engineering, University of Engineering & Technology, Faisalabad Campus, Lahore, Pakistan |
| Abstract: | The experimental results obtained from scratching a semicrystalline poly (ether ether ketone) surfaces, (PEEK), and its composites are presented in this paper. A semicrystalline PEEK and a carbon fiber oriented PEEK were scratched using conical indenters on a pendulum sclerometer. The carbon fiber oriented PEEK composites were scratched in the parallel, the orthogonal and the transverse direction to the fiber orientation. Subsequent deformations of the surfaces were assessed through subjective evaluation of the images obtained from a scanning electron microscope (SEM). The semicrystalline PEEK samples were found to be deformed by ductile ploughing and brittle deformation mechanism. In addition a fibrillation of the crystalline lamella of the polymer was also seen to be formed in case of severe brittle deformations. Fiber matrix debonding, matrix material debris formation, and fiber breakage were observed to be the dominant deformation mechanisms of the carbon fiber oriented composites. The scratch deformations of fiber oriented polymers were found to be highly dependent on fiber orientation angle relative to the scratching direction. |
| Keywords: | |
| 本文献已被 SpringerLink 等数据库收录！ | |