Fabrication and characterization of PET nanofiber hollow yarn |
| |
| Authors: | L Javazmi S A Hosseini Ravandi A A Ghareaghaji |
| |
| Institution: | 1. Department of Textile Engineering, Isfahan University of Technology, Isfahan, 84156, 83111, Iran
2. Department of Textile Engineering, Amirkabir University of Technology, Tehran, Iran
|
| |
| Abstract: | In this study, various concentrations of polyethylene terephthalate (PET) polymeric solution were investigated to produce hollow nanofiber yarn. First, the electrospining apparatus was designed in a way that to put PVA multifilament in the core and to twist PET nanofibers onto multifilament yarn as a sheath simultaneously, followed by dissolving PVA yarn in hot water, PET hollow nanofiber yarn was produced. In this survey, it has been observed that the average thickness of sheath increased by increasing concentrations of PET polymeric solution. Results showed that maximum efficiency of extracting the PVA multifilament from the hollow yarn under certain conditions (concentration of 18 % (w/v) of PET, applied voltage of 10 kV, and flow rate of 0.0526 ml/h) was more than 85 %. The mechanical and physical properties of PET hollow yarns were investigated and indicated that the hollow nanofiber yarns at concentration of 30 % and 18 % polymeric solution had the lowest strength and the highest regain moisture, respectively. |
| |
| Keywords: | |
| 本文献已被 SpringerLink 等数据库收录！ |
|