Microfracture in wood monitored by confocal laser scanning microscopy
Authors:G Dill-Langer  S Lütze  S Aicher
Institution:(1) Department of Mechanical Engineering, Albert Nerken School of Engineering, The Cooper Union for the Advancement of Science and Art, 51 Astor Place, New York City, NY 10003, USA;(2) Department of Mechanical Engineering, Tuskegee University, Tuskegee, AL 36088, USA
Abstract:The paper deals with the experimental characterisation of damage evolution within the radial (R)–tangential (T) growth plane of softwood loaded in tension perpendicular to the grain. The reported investigations comprise in-situ monitoring of crack propagation by means of Confocal Laser Scanning Microscopy (CLSM) and evaluations of crack patterns of broken specimens. Three types of notched specimens, representing different crack propagation systems, were tested; for all configurations, both, loading and crack propagation direction were located within the RT plane of wood. The CLSM pictures of broken specimens show distinct differences among the regarded configurations with respect to crack paths. Two different damage mechanisms were identified being rupture of earlywood cell walls in the case of crack propagation in tangential direction and debonding of wood fibers, i.e. rupture of the interface zone between adjacent tracheids, in case of crack progression in radial direction. In the case of an intermediate crack system with an angle of 45° between initial notch direction and radial direction the crack evolution was monitored in-situ during the tension test, whereby the combined action of both basic fracture mechanisms was observed.
Keywords:
本文献已被 SpringerLink 等数据库收录!
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号