High performance fibers production process using Taguchi experimental design |
| |
Authors: | Hossein Ahmadi Danesh Ashtiani Reza Eslami Farsani |
| |
Institution: | (1) Department of Biomaterials, Faculty of Material Science and Ceramics, AGH University of Science and Technology, Al. Mickiewicza 30, 30-059 Krakow, Poland;(2) Department of Man-Made Fibers, Faculty of Textile Engineering and Marketing, Technical University of Lodz, ul. Zeromskiego 116, 90-926 Lodz, Poland; |
| |
Abstract: | In this research, results of an experimental interaction effect of operating parameters on tensile strength carbon fibers
from a commercial PAN-based precursor are investigated. Ten parameters at two and four levels (L32=21×49) were investigated: stabilization temperature at first stage (STFIS), stabilization duration time at first stage (SDTFIS),
stabilization temperature at second stage (STSS), stabilization duration time at second stage (SDTSS), stabilization temperature
at third stage (STTS), stabilization duration time at third stage (SDTTS), stabilization temperature at fourth stage (STFOS),
stabilization duration time at fourth stage (SDTFOS), carbonization temperature (CT), and carbonization duration time (CDT).
In this study, Taguchi method was used initially to plan a minimum number of experiments. Statistical analysis, analysis of
variance (ANOVA), was also employed to determine the relationship between experimental conditions and yield levels. ANOVA
was applied to calculate sum of square, variance, ratio of factor variance to error variance and contribution percentage of
each factor on response. The results show that increasing all of parameters improves tensile strength performance. The optimum
levels of influential factors, determined for tensile strength are STFIS 200 °C, SDTFIS 120 min, STSS 225 °C, SDTSS 120 min,
STTS 240 °C, SDTTS 120 min, STFOS 260 °C, SDTFOS 60 min, CT 1400 °C and CDT 10 min. The results showed that CT and ODTFIS
are the most and the less effective factors on response, respectively. |
| |