| 小麦茎秆抗拉性能研究 |
| |
| 引用本文： | 赵多佳,郭维俊,宋言明,陈建恩,刘鹏霞.小麦茎秆抗拉性能研究[J].安徽农业科学,2008,36(14):5837-5839. |
| |
| 作者姓名： | 赵多佳 郭维俊 宋言明 陈建恩 刘鹏霞 |
| |
| 作者单位： | 甘肃农业大学工学院,甘肃兰州,730070;甘肃农业大学工学院,甘肃兰州,730070;甘肃农业大学工学院,甘肃兰州,730070;甘肃农业大学工学院,甘肃兰州,730070;甘肃农业大学工学院,甘肃兰州,730070 |
| |
| 基金项目： | 甘肃省教育厅项目资助. |
| |
| 摘 要： | 目的]分析小麦茎秆的抗拉能力。方法]以水分含量51.3%、自然状态下干燥的0158-2小麦成熟期去鞘茎秆为材料,研究小麦茎秆的抗拉能力。结果]由应力-应变曲线可知,随着变形的增大,应力逐渐增大,达到最大值时出现断裂。由负荷-时间曲线可知,随着时间的变化,负荷线性增大。负荷随着变形的增大而增大。水分为51.3%时小麦茎秆的弹性模量范围为1 012.0～1 511.0 MPa,强度极限范围为30.9～134.7 MPa;干燥时小麦茎秆的弹性模量范围为2 672.3～4 593.0 MPa,强度极限范围为29.8～119.0 MPa。水分含量越高,小麦茎秆的弹性模量越小,强度极限也越小。结论]小麦茎秆水分为51.3%时,其弹性模量为1 278.2 MPa,强度极限为64.6 MPa;茎秆干燥时其弹性模量为3 114.7 MPa,强度极限为78.0 MPa。
|
| 关 键 词： | 弹性模量 拉力 应力 应变 |
| 文章编号： | 0517-6611(2008)14-05837-02 |
| 修稿时间： | 2008年3月19日 |
Experimental Analysis of the Tensile Properties of Wheat Stalk |
| |
| ZHAO Duo-jia.Experimental Analysis of the Tensile Properties of Wheat Stalk[J].Journal of Anhui Agricultural Sciences,2008,36(14):5837-5839. |
| |
| Authors: | ZHAO Duo-jia |
| |
| Abstract: | Objective] The aim of the research was to analyze the tensile ability of wheat stalk.Method] With naturally-dried wheat stalk of 0158-2 in mature period with water content of 51.3% whose sheath was removed as materials,the tensile ability of wheat stalk was studied.Result] The stress-strain curve showed that the stress gradually increased with the augment of deformation and rupture appeared when the stress reached the maximum.The load-time curve showed that the load showed a linear increase with the changes of time.And the load was increased with the augment of deformation.When water content was 51.3%,the elastic modulus range of wheat stalk was 1 012.0-1 511.0 MPa and the intensity limit range was 30.9-134.7 MPa.Under dying situations,the elastic modulus range of wheat stalk was 2 672.3-4 593.0 MPa and the intensity limit range was 29.8-119.0 MPa.The higher water content was,the smaller the elastic modulus and the intensity limit were.Conclusion] When water content of wheat stalk was 51.3%,the elastic modulus of wheat stalk was 1 278.2 MPa and its intensity limit was 64.6 MPa.Under dying situations,the elastic modulus of wheat stalk was 3 114.7 MPa and its intensity limit was 78.0 MPa. |
| |
| Keywords: | Elastic modulus Pull Stress Strain |