Biomechanical properties of braided polyester tapes intended for use as intra-articular cranial cruciate ligament prostheses in dogs |
| |
| Authors: | de Rooster H Vangheluwe L van Bree H Ledoux M Van Langenhove L |
| |
| Institution: | Department of Diagnostic Imaging of Domestic Animals, Faculty of Veterinary Medicine, Ghent University, Merelbeke, Belgium. |
| |
| Abstract: | OBJECTIVE: To determine the in vitro structural and material properties of braided, multifilament, nonabsorbable polyester tapes, used for intra-articular stabilization of cranial cruciate ligament- (CCL-) deficient stifle joints in dogs, and compare those with properties of multifilament polyamide tapes. SAMPLE POPULATION: 30 polyester tapes (width, 4 mm), 10 polyester tapes (width, 7 mm), and 30 polyamide tapes (width, 4 mm) were tested to failure. Cyclic loading experiments were also performed, using 3 polyester tapes of each width. PROCEDURE: Tapes were mounted in a tensile tester as single loops, simulating intra-operative conditions, and elongated to failure at 1,000 mm/min. Additionally, the behavior of polyester tapes was tested at different elongation rates. In a second series of experiments, biomechanical variables of the polyester tapes were measured after 25 sets of 2,000 cycles between physiologic force limits. RESULTS: Mean (+/- SD) ultimate loads of the 4-mm wide polyamide tapes, 4-mm wide polyester tapes, and 7-mm wide polyester tapes were 266.48 +/- 13.19 301.78 +/- 16.92, and 726.40 +/- 37.74 N, respectively. Corresponding stiffnesses were 15.57 +/- 0.49, 21.63 +/- 2.19, and 34.85 +/- 2.66 N/mm, respectively. Failure properties of polyester tapes were affected by previous cyclic loading. CONCLUSIONS AND CLINICAL RELEVANCE: Polyester tapes of 4- or 7-mm widths should be able to resist forces resulting from weight bearing in dogs, suggesting that these tapes will be effective for stabilization of the stifle joint in dogs with a ruptured CCL. |
| |
| Keywords: | |
| 本文献已被 PubMed 等数据库收录！ |
|