Characterization of cellulose in compression and opposite woods of a Pinus densiflora tree grown under the influence of strong wind |
| |
| Authors: | F Tanaka T Koshijima K Okamura |
| |
| Institution: | (1) Wood Research Institute, Kyoto University, Uji, Kyoto, Japan;(2) Faculty of Agriculture, Kyoto University, Kyoto, Japan |
| |
| Abstract: | Summary Structural factors in a Pinus densiflora tree grown under the influence of strong wind were measured. No
difference for cellulose molecules was noticed between compression and opposite wood, but the
was somewhat lower in the region where the compression wood was concentrated. The degree of crystallinity of cellulose was 45–50% in compression wood, about 50% in normal wood, and 50–60% in opposite wood. The crystallinity decreased with increasing height above the ground. The maximum point of crystallographic b-axis (fiber axis) orientation distribution for cellulose crystallites in compression wood was located at   30°, in normal wood at 25° and in opposite wood at 0°. The cellulose crystallite dimension in the transverse direction was 3.2 nm, corresponding to four cellulose unit cells, a value that was almost constant throughout the wood. In the longitudinal direction, there were large differences in cellulose crystallite dimensions between compression and opposite woods. In compression wood the cellulose crystallite dimensions was 12 nm corresponding to 11–12 cellulose unit cells. In opposite wood it was 17–32.5 nm corresponding to 17–32 cellulose unit cells. These structural factors were apparently affected by the environmental conditions, and the mechanical properties of the wood were influenced by these factors. Opposite wood had longer crystallites, a higher degree of crystallinity and a better orientation distribution of cellulose crystallites in the longitudinal direction. Compression wood, on the other hand, had shorter crystallites, a lower degree of crystallinity and a large angle between the stem and the direction of the crystallites. |
| |