| 杉木积成材制造工艺研究 |
| |
| 引用本文： | 杜春贵,刘志坤,张齐生.杉木积成材制造工艺研究[J].林业科技,2009,34(4):48-50. |
| |
| 作者姓名： | 杜春贵 刘志坤 张齐生 |
| |
| 作者单位： | 浙江林学院工程学院,临安,311300 |
| |
| 基金项目： | 浙江省“十五”攻关重点项目(011102164);;国家与浙江省农业科技成果转化资金项目(03EFN213300104、2003D70078) |
| |
| 摘 要： | 研究以杉木制材板皮为原料，采用梳解加工法制造杉木积成材的制板工艺。结果表明，密度为0．6g／cm^3，厚为16mm的杉木积成材，其较佳制造工艺为木束条含水率6％-9％，施胶量8％-9％，热压压力2．0MPa，热压温度160℃。热压时间10min。
|
| 关 键 词： | 杉木制材板皮 杉木积成材 制造工艺 性能 |
Study on Manufacturing Technology of Chinese Fir OLSL |
| |
| DU Chungui.Study on Manufacturing Technology of Chinese Fir OLSL[J].Forestry Science & Technology,2009,34(4):48-50. |
| |
| Authors: | DU Chungui |
| |
| Institution: | Zhejiang Forestry College;Lin'an 311300 |
| |
| Abstract: | Using sawmill slabs of Chinese fir as the basic material by combing method, and the manufacturing technology was studied. The results show that the better manufacturing technology parameters of Chinese fir OLSL for the density was 0. 6g/cm^3, and thickness was 16mm are as follows. The moisture content wood stick was 6% -9%. The resin content of wood stick was 8% -9%. The hot pressing pressure was 2. 0MPa. The hot pressing temperature was 160℃. The hot pressing time was 10min. |
| |
| Keywords: | Sawmill slab of Chinese fir Chinese fir oriented laminated stick lumber （Chinese fir OLSL） Manufacturing technology Properties |