| 美国花旗松锯材剩余物的制浆造纸性能 |
| |
| 引用本文： | 张利萍,王书强,孙夏杰,高慧.美国花旗松锯材剩余物的制浆造纸性能[J].福建农业大学学报,2014(3):327-331. |
| |
| 作者姓名： | 张利萍 王书强 孙夏杰 高慧 |
| |
| 作者单位： | 安徽农业大学林学与园林学院,安徽合肥230036 |
| |
| 基金项目： | 安徽省自然科学基金资助项目（1208085MC37）. |
| |
| 摘 要： | 以美国花旗松锯材剩余物为原料，对其化学组分、纤维形态以及制浆造纸性能进行测定与分析．结果表明：冷水抽提物、热水抽提物、1％NaOH抽提物的含量分别为13．82％、17．04％和23．95％；klason木质素含量为26．57％；综纤维、α纤维素、半纤维索的含量分别为75．44％、50．65％和24．79％；戊聚糖含量为8．59％．纤维的平均长度、平均宽度、腔径、双壁厚分别为3263、17．68、11．14、6．51μm；纤维的长宽比和壁腔比分别为184和0．63；纤维的结晶度为50．85％．制浆造纸的最佳方法是硫酸盐蒽醌法．最佳条件为用碱量23％、硫化度28％、保温时间210min、蒽醌用量为0．1％．此时，残碱为5．61g·L-1；粗浆得率为45．34％，卡伯值为17．79，特性粘度为1039．30mL·g-1，纸张的抗张强度为76．17Nm·g-1，撕裂指数为24．62mN·m2·g-1，耐破指数为5．32kPa·ms·g-1，综合强度为20．13．
|
| 关 键 词： | 美国花旗松锯材剩余物 化学组分 纤维形态 制浆造纸 |
Pulping and papermaking performance of lumber residues of Pseudotsuga menziesii |
| |
| ZHANG Li-ping,WANG Shu-qiang,SUN Xia-jie,GAO Hui.Pulping and papermaking performance of lumber residues of Pseudotsuga menziesii[J].Journal of Fujian Agricultural University,2014(3):327-331. |
| |
| Authors: | ZHANG Li-ping WANG Shu-qiang SUN Xia-jie GAO Hui |
| |
| Institution: | (College of Forestry and Gardening, Anhui Agricultural University, Hefei, Anhui 230036, China) |
| |
| Abstract: | Lumber residue of Pseudotsuga menziesii was selected, and its chemical composition, fiber morphology and pulping andpapermaklng performance were measured. It was observed that the content of cold water extractive, hot water extractive and 1%NaOH extractive was 13.82%, 17.04% and 23.95%, respectively. The content of klason lignin was 26.57%. The content of halo-cellulose, ct cellulose, hemicellulose and pentosan was 75.44%, 50.65%, 24.79% and 8.59%, respectively. The average fiberlength, the fiber width and the ratio of them were 3263 pin, 17.68 pan and 184. The double cell wall thickness, the lumen diame-ter, and the ratio of them were 6.51 p.m, 11.14 pan and 0.63. The percent of fiber crystallinity was 50.85%. The best pulpingmethod was regarded as sulphate-anthraquinone. The optimum conditions of pulping were alkali 23%, sulfidity 28% and holdingtime 210 rain. Under these conditions, the residual alkali was 5.61 g ·g-1, and the pulp yield, the kappa number, the intrinsicviscosity was 45.34%, 17.79 and 1039.30 mL · g-1 respectively. The tensile strength, tear index, bursting strength index and thecomprehensive strength of the paper was 76.17 Nm · g-1, 24.62 Nm · m2 ·g-1, 5.32 kPa ·g-1 and 20.13, respectively. |
| |
| Keywords: | lumber residues of Pseudotsuga menziesii chemical composition fiber morphology pulping and papermaking |